期刊
JOURNAL OF APPLIED PHYSICS
卷 88, 期 1, 页码 210-222出版社
AMER INST PHYSICS
DOI: 10.1063/1.373645
关键词
-
We report on our observation of visible photoluminescence and cathodoluminescence of Pr-implanted GaN. The implanted samples were subjected to isochronal thermal annealing treatments at a temperature of 1100 degrees C in N-2 at atmospheric pressure to recover from implantation damage and activate the rare earth ions. The sharp characteristic emission lines corresponding to Pr3+ intra-4f(n)-shell transitions are resolved in the spectral range from 400 to 1000 nm and observed over the temperature range from 12 to 335 K. We have developed an energy level diagram for Pr3+ ions in GaN using recorded spectra. The photoluminescence decay kinetics measurements of P-3(1), P-3(0), and D-1(2) levels and quenching mechanism analysis allow us to conclude that the dominant de-excitation process is of electric dipole-electric quadrupole type. We found also that the D-1(2) level separated from the upper P-3(0) level by 3755 cm(-1) energy gap can be populated in several ways, by direct energy transfer processes, cross relaxation \P-3(0),H-3(4)]-->\D-1(2),H-3(6)] and cascade processes from the P-3(0) or higher levels. The full width at half maximum of the strongest photoluminescence line at 653 nm, the P-3(0) level, is 2.9 meV at 13 K, with a 1.86 meV blue peak shift in going from 13 to 330 K temperature, while the line at 670 nm, P-3(1) level, has a full width at half maximum of 4 meV at 13 K and a 1.6 meV red peak shift. The thermal stability of GaN:Pr3+ epilayers indicates the suitability of this material for visible optoelectronic devices. (C) 2000 American Institute of Physics. [S0021-8979(00)01613- 3].
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据