JOURNAL OF COLLOID AND INTERFACE SCIENCE
卷 227, 期 2, 页码 445-451出版社
ACADEMIC PRESS INC
DOI: 10.1006/jcis.2000.6873
关键词
layered double hydroxides; organo-clay; grafting
Zn-Al-CO3 layered double hydroxide was synthesized at room temperature using a procedure reported elsewhere. After characterization, 0.5 g of the Zn-Al-CO3 layered compound was reacted under air with 15 cm(3) of ethylene glycol at 80 degrees C for a period of 5 days. After washing with acetone and drying at 50 degrees C, the resulting white powder was characterized by X-ray powder diffraction, thermal analysis (simultaneous TG/DSC), elemental analysis (C, H, N, Al, and Zn content), and FTIR spectroscopy. All of the experimental data were consistent with the bidentade grafting of ethylene glycol into the interlayer surface of the Al-Zn double hydroxide. The stoichiometry obtained [Zn0.66Al0.34(OCH2CH2O)](OH)(0.34).0.4H2O] showed that all of the surface hydroxide groups were replaced by ethylene glycol through Al-(Zn)-O-C bonds. Carbonate could not be detected by FTIR, proving that OH- was probably the actual intercalated counteranion. (C) 2000 Academic Press.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据