期刊
OXIDATION OF METALS
卷 54, 期 1-2, 页码 63-71出版社
SPRINGER/PLENUM PUBLISHERS
DOI: 10.1023/A:1004698528721
关键词
microstructure; Inconel 625; oxidation; deformation substructure; deformation twins; energy-dispersive spectroscopy (EDS); internal oxide
The high-temperature, isothermal-oxidation behavior of a superalloy was studied in the as-rolled and deformed conditions. The microstructural changes occurring during the oxidation of samples were examined using optical, scanning electron microscopy (SEM), fine-probe EDS microanalysis, and X-ray diffraction techniques. The topography of the oxide layers formed in the as rolled and cold-deformed specimens exposed at various temperatures and time intervals is also examined The kinetics and microstructural results are presented for the comparative study of the structural changes occurring during high-temperature oxidation. It was found that a Cr2O3 external layer was adherent and uniform on the rolled specimens in comparison to the scattered and preferential oxide developed on the deformed specimens, The latter can be attributed to the concurrent dynamic changes occurring in the deformed substructure that subsequently lead to breaking and spallation of the oxide.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据