期刊
THERMOCHIMICA ACTA
卷 357, 期 -, 页码 89-95出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/S0040-6031(00)00372-5
关键词
PBXs; Kel F 800; nitroplasticizer; estane; glass-transition temperature (T-g); HMX; TATB
Various plastic bonded explosives (PBXs) contain about 5 wt.% polymer, plasticizer, and stabilizer as binder. The glass-transition temperature (T-g) determines, in part, if the binder will reduce or increase the sensitivity of the PBX to impact. A soft binder reduces the impact sensitivity; however, too soft a binder compromises the mechanical strength below that desirable for dimensional stability. Glass transitions were measured by temperature modulated DSC for PBXs before and after pressing. Pressing temperature was 90 degrees C. The T-g of Estane, a polyester/polyurethane used in some PBX binders, was investigated. Only small changes were observed in the low temperature T-g of the soft segments but larger changes were seen in the higher temperature transitions due to the relaxation of the hard segments. The T-g of Kel F 800, a binder used in insensitive PBX 9502, was observed near ambient temperature. The PBX 9502 had a lower T-g than the neat polymer. Mechanical strength was measured for the samples of PBX 9502. (C) 2000 Elsevier Science B.V. Ail rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据