期刊
JOURNAL OF APPLIED PHYSICS
卷 88, 期 7, 页码 4257-4264出版社
AMER INST PHYSICS
DOI: 10.1063/1.1309040
关键词
-
The lattice deformation of dense strained La0.7Sr0.3MnO3 (LSMO) films is shown to control the easy direction of the magnetization. Optimized pulsed laser deposited conditions allow the fabrication of dense LSMO thin films which present an exceptional flatness with a peak-valley roughness (Rp-v) of 1 Angstrom, associated to epitaxial grains as large as 1 mu m. Electron microscopy coupled with x-ray diffraction have been used to study the unit cell distortion of both tensile and compressive dense LSMO films as a function of the thickness. No relaxation of the lattice distortion imposed by substrate has been observed in the thickness range 10-60 nm. The Curie temperature is not significantly affected by the nature of the substrate: a T-C of 350 K is observed for both SrTiO3 (STO) and LaAlO3 (LAO) substrates, i.e., close to the bulk material (369 K). In contrast, the easy direction of magnetization depends on the substrate. For tensile films deposited on the STO substrate, the unit cell is elongated along the film's plane (a(in-plane) = 3.905 Angstrom) with a reduced perpendicular parameter (c(perp) = 3.85 Angstrom): an easy direction of magnetization M in the plane of the film is observed. For compressive films deposited on LAO substrate, the situation is reversed with a unit cell elongated along the direction of growth (c(perp) = 4.00 Angstrom and a(in-plane) = 3.79 Angstrom) and an easy axis for M along this perpendicular out-plane direction. It is thus demonstrated that the larger cell parameter, a(in-plane) for films deposited on STO and c(perp) for films deposited on LAO, is fully correlated to the direction of the easy magnetization. (C) 2000 American Institute of Physics. [S0021-8979(00)08020-8].
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据