Microstructural development of neutron irradiated W-Re alloys

Tungsten (W) alloys are candidate materials to be used as high-heat-flux materials in fusion reactors. In our previous work, W-26 wt% Re showed drastic hardening and embrittlement after the neutron irradiation. In this study, to clarify the irradiation hardening and embrittlement behavior of W-26 wt% Re, from the viewpoint of microstructural development, the microstructure observation of the neutron irradiated W-26 wt% Re was carried out using transmission electron microscope (TEM). The specimens were irradiated at the materials open test assembly of the fast flux test facility (FFTF/MOTA-2A cycle 11) up to similar to1 x 10(27) n/m(2), (E-n > 0.1 MeV). The irradiation temperatures were 646, 679, 792, 873 and 1073 K. In all neutron irradiated W-26 wt% Re samples, sigma-phase precipitates and chi-phase precipitates were observed, while in the thermally aged specimen, only sigma-phase precipitates were observed. Irradiation effects on microstructural development are discussed. (C) 2000 Elsevier Science B.V. All rights reserved.