Gd-2(Ti2-xZrx)O-7 samples with 0 less than or equal to x less than or equal to 1.5 were single-phase and pyrochlore structured after sintering at 1600 degreesC in air. The Gd2Zr2O7 (x = 2) end member predominantly displayed an anion deficient-fluorite structure. Raman spectroscopy indicated that the level of short-range fluorite-like disorder in the unirradiated Gd-2(Ti2-xZrx)O-7 samples increased significantly as Zr was substituted for Ti, despite the retention of a long-range pyrochlore structure for samples with 0 less than or equal to x less than or equal to 1.5. Glancing-incidence X-ray diffraction indicated that pyrochlores with an ionic radii ratio r(A)/r(B) less than or equal to 1.52(x greater than or equal to 1.5) were transformed into a radiation resistant defect-fluorite structure after irradiation at room temperature with 2 MeV AU(2+) to fluence of 5 ions/nm(2). As the ionic radii ratio of the pyrochlore increased beyond r(A)/r(B) > 1.52, the defect-fluorite structure became increasingly unstable with respect to the amorphous state under identical irradiation conditions. Crown Copyright (C) 2001 Published by Elsevier Science B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据