Correlation of plastic deformation and dynamic recrystallization in magnesium alloy Zk60

期刊

ACTA MATERIALIA
卷 49, 期 7, 页码 1199-1207

出版社

PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/S1359-6454(01)00020-9

关键词

dislocations; deformation mechanisms; microstructure; recrystallization & recovery

向作者/读者索取更多资源

The mechanisms of plastic deformation and dynamic recrystallization (DRX) in a Mg-5.8% Zn-0.65% Zr alloy were studied by compression tests at temperatures between 423 and 723 K and at strain rates ranging From 10(-5) to 10(-1) s(-1). It was shown that the mechanisms of DRX depended on the operating deformation mechanisms which changed with temperature. Low-temperature DRX (LTDRX below 473 K) was associated with the operation of twinning, basal slip and (a+c) dislocation glide. In the intermediate temperature range (473-523 K) continuous DRX (CDRX) was observed and associated with extensive cross-slip due to the Friedel-Escaig mechanism. At temperatures ranging from 573 to 723 K bath bulging of original grain boundaries and subgrain growth were the operating DRX mechanisms and controlled by dislocation climb. (C) 2001 Acta Materialia Inc. Published by Elsevier Science Ltd. All rights reserved.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.7
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据