NiFe2O4 nanoparticles were prepared by the sol-gel method using polyacrylic acid (PAA) as a chelating agent. it was shown that pure spinel NiFe2O4 nanoparticles with a diameter of 5 similar to 30 nm and a specific surface area of 20.0 similar to 55.2 m(2)/g could be produced by calcining the gel precursors with various molar ratios of PAA to total metal ions (0.5 similar to2.0) in air at 300 degreesC for 2h. As the molar ratio of PAA to total metal ions increased, particle sizes decreased but the crystallinity increased, revealing PAA not only worked as a chelating agent to disperse the cations homogeneously but also contributed its combustion heat to increase the crystallinity of NiFe2O4 nanoparticles. Moreover, the magnetic analysis showed the resultant NiFe2O4 nanoparticles might be superparamagnetic. Their saturation magnetization (0.19 emu/mol at 298 K) was slightly lower than that for bulk materials due to small size and increased slightly with decreasing the temperature below 360 K (C) 2001 Elsevier Science Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据