Spatially resolved X-ray diffraction mapping of phase transformations in the heat-affected zone of carbon-manganese steel arc welds

Phase transformations that occur in the heat-affected zone (HAZ) of gas tungsten are welds in AISI 1005 carbon-manganese steel were investigated using spatially resolved X-ray diffraction (SRXRD) at the Stanford Synchrotron Radiation Laboratory. In situ SRXRD experiments were performed to probe the phases present in the HAZ during welding of cylindrical steel bars. These real-time observations of the phases present in the HAZ were used to construct a phase transformation map that identifies five principal phase regions between the liquid weld pool and the unaffected base metal: (1) alpha -ferrite that is undergoing annealing, recrystallization, and/or grain growth at subcritical temperatures, (2) partially transformed alpha -ferrite co-existing with gamma -austenite at intercritical temperatures, (3) single-phase gamma -austenite at austenitizing temperatures, (4) delta -ferrite at temperatures near the liquidus temperature, and (5) back transformed alpha -ferrite co-existing with residual austenite at subcritical temperatures behind the weld. The SRXRD experimental results were combined with a heat flow model of the weld to investigate transformation kinetics under both positive and negative temperature gradients in the HAZ. Results show that the transformation from ferrite to austenite on heating requires 3 seconds and 158 degreesC of superheat to attain completion under a heating rate of 102 degreesC/s. The reverse transformation from austenite to ferrite on cooling was shown to require 3.3 seconds at a cooling rate of 45 degreesC/s to transform the majority of the austenite back to ferrite; however, some residual austenite was observed in the microstructure as far as 17 mm behind the weld.