Improved interfacial resistance was observed in lithium cells by the use of new additives. The additives, nitrile sucrose and nitrile cellulose and their lithium salts, were evaluated in polyvinylidene difluoride (PVDF) thin-film gelled electrolytes containing a mixture of ethylene carbonate (EC) and diethyl carbonate (DEC). The electrochemical properties of the films with and without the additives were measured as a function of temperature and compared. The interfacial resistance (R-in) of the films with the additives was significantly lower than that without the additives, especially at sub-ambient temperatures. For example, the R-in at -20 degreesC for the films with additives was around 7000 Ohm cm(2) and that for the films without the additives was > 20.000 Ohm cm(2).]Results obtained from using the additives in lithium-ion (Li-ion) cells show significant improvements in the low frequency resistance of the cells. (C) 2001 Published by Elsevier Science B.V.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据