JOURNAL OF THERMAL SPRAY TECHNOLOGY
卷 10, 期 2, 页码 326-336出版社
ASM INTERNATIONAL
DOI: 10.1361/105996301770349411
关键词
diagnostics; imaging; plasma spectroscopy; temperature field
An experimental study was conducted to determine the plasma temperature held and its parametric variation with respect to plasma operating conditions using emission spectroscopy. The focus of our study was the direct current (DC) are plasma systems used in thermal spray processing of ceramic materials. A commercial plasma system (Metco 9M series) was operated with mixtures of argon and hydrogen in the power input range from 12 to 36 kW, Temperature measurements were based on the detection of emission line intensities from Ar-I neutral species, Spatially resolved measurements were obtained of the plasma temperatures in axisymmetric plasma jets using Abet deconvolution, The variation of plasma axial and radial temperature distributions was measured as a function of the plasma input power, the total gas how rate, and the binary gas composition of argon and hydrogen, Time-averaged plasma gas temperatures were found to increase with increasing plasma input power, increasing hydrogen content of the plasma gas, and decreasing total gas flow rate, Plasma temperatures decrease progressively with increasing distance from the nozzle exit, The peak temperatures near the nozzle exit are in the range of 12,500 to 14,000 K, The radial temperature profiles show an approximately self-similar decay in the near field of these plasma jets, It was also determined from time resolved intensity measurements that there are significant fluctuations in the argon emission intensity with increasing hydrogen fraction in the mixture, These fluctuations with a typical frequency of 5.2 kHz are attributed to the are root instabilities observed before, Finally, the measured plasma temperature field is empirically correlated in terms of radial and axial coordinates, plasma electrical input power, plasma efficiency, and gas composition, These temperature data can be used to validate numerical simulations as well as in choosing locations where different materials can be introduced into the plasma jets. This is particularly important for nanostructured materials, which loose their structure upon melting as a result of being exposed to high plasma temperatures.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据