期刊
JOURNAL OF THE AMERICAN CHEMICAL SOCIETY
卷 123, 期 31, 页码 7497-7505出版社
AMER CHEMICAL SOC
DOI: 10.1021/ja010235q
关键词
-
Structurally well-defined polymer-nanoparticle hybrids were prepared by modifying the surface of silica nanoparticles with initiators for atom transfer radical polymerization and by using these initiator-modified nanoparticles as macroinitiators. Well-defined polymer chains were grown from the nanoparticle surfaces to yield individual particles composed of a silica core and a well-defined, densely grafted outer polystyrene or poly(methyl methacrylate) layer. In both cases, linear kinetic plots, linear plots of molecular weight (M-n) versus conversion, increases in hydrodynamic diameter with increasing conversion, and narrow molecular weight distributions (M-w/M-n) for the grafted polymer samples were observed. Polymerizations of styrene from smaller (75-nm-diameter) silica nanoparticles exhibited good molecular weight control, while polymerizations of methyl methacrylate (MMA) from the same nanoparticles exhibited good molecular weight control only when a small amount of free initiator was added to the polymerization solution. The difference in polymerization behavior for styrene and MMA was ascribed to the facts that styrene undergoes thermal self-initiation while MMA does not and that termination processes involving freely diffusing chains are faster than those involving surface-bound chains. The polymerizations of both styrene and MMA from larger (300-nm-diameter) silica nanoparticles did not exhibit molecular weight control. This lack of control was ascribed to the very high initial monomer-to-initiator ratio in these polymerizations. Molecular weight control was induced by the addition of a small amount of free initiator to the polymerization but was not induced when 5-15 mol % of deactivator (Cu(II) complex) was added.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据