CHEMISTRY OF MATERIALS
卷 13, 期 9, 页码 2905-2908出版社
AMER CHEMICAL SOC
DOI: 10.1021/cm010126a
关键词
-
AuBa2Ca2Cu3O9 (Au-1223-Ba) and AuBa2Ca3Cu4O11 (Au-1234-Ba), two high-T-c superconductors, were synthesized by high-pressure/high-temperature at 6 GPa and 1250-1300 degreesC. These phases are the third and fourth members of the AuBa2Can-1CunO2n+3 series. The Au-1223-Ba and Au-1234-Ba phases crystallize in an orthorhombic primitive system with the lattice parameters a = 3.8182(4) Angstrom, b = 3.8555(4) Angstrom, and c = 15.445(2) Angstrom, and a = 3.8266(3) A, b = 3.8505(3) A, and c = 18.494(1) A, respectively. The Au-1234-Ba phase showed bulk superconductivity below 99 K. The superconducting transition of the as-grown Au-1223-Ba sample was very broad with a transition temperature of approximate to 30 K and with a small superconducting volume fraction. The volume fraction increased after the sample was postannealed at 300 degreesC in O-2 atmosphere.