期刊
PHILOSOPHICAL MAGAZINE LETTERS
卷 81, 期 10, 页码 709-718出版社
TAYLOR & FRANCIS LTD
DOI: 10.1080/09500830110073959
关键词
-
The quasicrystal structure of primary intermetallic particles found in the as-cast microstructure of a permanent mould-cast Mg-8 wt% Zn-4 wt% Al alloy has been characterized using transmission electron microscopy. Most primary intermetallic particles have an average composition of Mg9+/-2Zn4+/-1Al3+/-1 and a primitive icosahedral structure, with a quasilattice parameter of 0.515 nm and a point group of m (3) over bar(5) over bar. The metastable quasicrystalline phase persists for extended periods at elevated temperatures; while the volume fraction decreases with thermal exposure at 325 degreesC, the decrease is small up to 120 h and a fraction persists after 720 h. There is no evidence of transformation of or within the quasicrystalline phase during this period. Instead, the metastable quasicrystalline phase is gradually replaced by the equilibrium Phi phase (Mg-21(Al, Zn)(17); space group, Pbcm). The relationship between the quasicrystalline phase, its cubic approximant T phase (Mg-32(Al, Zn)(49); space group, Im (3) over bar) and the Phi phase is discussed.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据