期刊
JOURNAL OF APPLIED PHYSICS
卷 90, 期 8, 页码 3843-3849出版社
AMER INST PHYSICS
DOI: 10.1063/1.1401803
关键词
-
Atomic force microscopy, transmission electron microscopy, optical, and magneto-optical microscopy have been used to study how structural and magnetic properties are changed when a Co/Pt multilayer is quasihomogeneously irradiated with Ga ions. Under low irradiation fluence, both grain size and texture in the multilayer increase. These effects continue for fluences in excess of 1 x 10(15) Ga ions/cm(2), but beyond this dose significant thinning of the multilayer is also observed. Three distinct irradiation-induced magnetic regimes with sharp transitions between each were identified. For Ga fluences less than 5 x 10(12) ions/cm(2), the irradiated region retains perpendicular uniaxial anisotropy but with coercivity lower than that of the as-grown film. For fluences between 5 x 10(12) and 1 x 10(13) Ga ions/cm(2), a transition from perpendicular to in-plane magnetization was experienced. Very little change of the in-plane magnetic properties of irradiated multilayers is then observed until the sample experiences a ferromagnetic to paramagnetic transition at fluences around 1 x 10(15) Ga ions/cm(2). A brief comparison with the effect of irradiating with He ions is given. (C) 2001 American Institute of Physics.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据