期刊
SURFACE & COATINGS TECHNOLOGY
卷 149, 期 2-3, 页码 179-184出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/S0257-8972(01)01451-7
关键词
thermal barrier coatings; delamination; thermal gradient; sintering; fracture toughness
Thermal barrier coating (TBC) systems are susceptible to delamination failures in the presence of a large thermal gradient. These failures, which occur within the TBC layer, are very different in character from those associated with the thermally grown oxide. Three possible causes of internal delamination are analyzed. In all cases, the thermomechanical properties of the TBC are allowed to vary because of sintering. (a) One mechanism relates to exfoliation of an internal separation in the TBC due to a through thickness heat flux. (b) Another is concerned with edge-related delamination within a thermal gradient. (c) The third is a consequence of sintering-induced stresses. The results of these analyses, when used in combination with available propel-ties for the TBC, strongly suggest that the second mechanism (b) predominates in all reasonable scenarios. Consequences for the avoidance of this failure mode are discussed. (C) 2002 Elsevier Science B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据