Electrochemical behavior of plasma-fluorinated graphite for lithium ion batteries

期刊

JOURNAL OF POWER SOURCES
卷 104, 期 1, 页码 108-114

出版社

ELSEVIER SCIENCE BV
DOI: 10.1016/S0378-7753(01)00895-3

关键词

plasma fluorination; surface modification; graphite electrode; lithium ion battery

向作者/读者索取更多资源

Electrochemical properties of plasma-fluorinated graphite samples have been investigated in 1 mol dm(-3) LiClO4 ethylene carbonate (EC)/diethyl carbonate (DEC) solution at 25 degreesC. Fluorine contents in plasma-fluorinated graphite samples were in the range of 0-0.3 at.% by elemental analysis and surface fluorine concentrations obtained by X-ray photoelectron spectroscopy (XPS) were in the range of 3-12 at.%. Raman spectroscopy revealed that surface disordering of graphite was induced by plasma fluorination. Plasma treatment increased the surface areas of graphite samples by 26-55% and the pore volumes for the mesopores with diameters of 1.5-2 and 2-3 nm. Plasma-fluorinated graphites showed capacities higher than those of original graphites and even higher than the theoretical capacity of graphite, 372 mAh g(-1), without any change of the profile of charge-discharge potential curves. The increments in the capacities were approximately 5, 10 and 15% for graphites with average particle diameters, 7, 25 and 40 mum, respectively. Furthermore, the coulombic efficiencies in first cycle were nearly the same as those for original graphites or higher by several percents. (C) 2002 Elsevier Science B.V. All rights reserved.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.8
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据