期刊
COLLOIDS AND SURFACES A-PHYSICOCHEMICAL AND ENGINEERING ASPECTS
卷 197, 期 1-3, 页码 7-17出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/S0927-7757(01)00683-5
关键词
silica; nanoparticle; semi-batch; statistical experimental method
Silica nanoparticles were prepared from tetraethylortho-silicate (TEOS) dissolved in ethanol by using a semi-batch process in order to control the particle properties. In this work, the statistical experimental method was also used to compare the properties (particle size and SD) of the SiO2 particles according to the four parameters (R = [H2O]/[TEOS]), concentration of ammonia (NH3), the feed rate of reactant, reaction temperature). We have obtained monodispersed silica particles having size ranging from 10 to 350 run by our experiment. It was found that the optimal synthesis conditions for the preparation of SiO2 nanoparticles with narrow size distribution in semi-batch process were as follows; (R [H2O]/[TEOS] 30-55; concentration of ammonia (NH3), 0.2-0.35 mole l(-1); feed rate of reactant, 13-17 cm(3) min(-1); reaction temperature, 55-65degreesC). The above-mentioned optimal conditions were used to prepare the particles with minimum particle size (30 nm) and its SD (< +/-5 nm), simultaneously. Experimental results measured by using the optimal synthesis conditions were in a good agreement with simulated value and the smallest size (similar to10 nm in diameter) was obtained. Also, we found that the effect of parameters on the particle size and SD in the preparation of SiO2 nanoparticles was increased in the following order; reaction temperature, (R = [H2O]/[TEOS]); concentration of ammonia (NH3), feed rate of reactant. (C) 2002 Elsevier Science B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据