期刊
POLYMER
卷 43, 期 8, 页码 2123-2132出版社
ELSEVIER SCI LTD
DOI: 10.1016/S0032-3861(02)00036-8
关键词
polymerization-filling technique; nanocomposite; metallocene
Polyethylene-layered silicate nanocomposites were prepared by the in situ intercalative polymerization of ethylene by the so-called polymerization-filling technique and analyzed by transmission electron microscopy (TEM), X-ray diffraction analysis (XRD), differential scanning calorimetry, dynamic mechanical analysis and tensile testing. Non-modified montmorillonite and hectorite were first treated by trimethylaluminum-depleted methylaluminoxane before being contacted by a Ti-based constrained geometry catalyst. The nanocomposite was formed by addition and polymerization of ethylene. In the absence of a chain transfer agent, ultra high molecular weight polyethylene was produced. The tensile properties of these nanocomposites were poor and essentially independent of the nature and content of the silicate. Upon hydrogen addition, the molecular weight of the polyethylene was decreased with parallel improvement of the tensile and shear moduli, in relation to the filler content. The exfoliation of the layered silicates was confirmed by XRD analysis and TEM observation. The mechanical kneading of the molten nanocomposites resulted in the partial collapse of the exfoliated structure driven by the thermodynamic stability of the layered filler. (C) 2002 Elsevier Science Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据