We investigate the effect of CH3CSNH2 solution treatment on Ti/Al ohmic contacts to n-GaN:Si (3x10(18) cm(-3)). It is shown that the sulfide treatment results in a drastic increase in the photoluminescence intensity, compared with that of the untreated sample. Current-voltage (I-V) results show that the sulfide treatment significantly improves the specific contact resistance. The annealing of the sulfide-treated sample (at 700 degreesC) results in a specific contact resistance of 3.1x10(-6) Omega cm(2). X-ray photoemission spectroscopy (XPS) results show that the Ga 2p core levels shift toward the higher-binding energy side by 0.2 eV for the sulfide-treated sample and by 0.4 eV for the annealed (sulfide-treated) sample, compared with that of the untreated one. It is further shown that the intensity of O 1s core level decreases with the sulfide treatment. Based on the I-V and XPS results, the sulfide and annealing treatment dependence of the specific contact resistance is discussed. (C) 2002 American Institute of Physics.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据