Strain and composition distributions within wurtzite InGaN/GaN layers are investigated by high-resolution reciprocal space mapping (RSM). We illustrate the potential of RSM to detect composition and strain gradients independently. This information is extracted from the elongation of broadened reciprocal lattice points (RLP) in asymmetric x-ray reflections. Three InxGa1-xN/GaN (nominal x=0.25) samples with layer thickness of 60, 120, and 240 nm, were grown in a commercial metal-organic chemical vapor deposition reactor. The RSMs around the (105) reflection show that the strain profile is nonuniform over depth in InGaN. The directions of pure strain relaxation in the reciprocal space, for a given In content (isocomposition lines), are calculated based on elastic theory. Comparison between these directions and measured distributions of the RLP shows that the relaxation process does not follow a specific isocomposition line. The In mole fraction (x) increases as the films relax. At the start of growth all the films have xsimilar to0.2 and are coherent to GaN. As they relax, x progressively increases towards the nominal value (0.25). Compositional gradients along the growth direction extracted from the RSM analysis are confirmed by complementary Rutherford backscattering measurements. (C) 2002 American Institute of Physics.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据