ELECTROCHIMICA ACTA
卷 47, 期 17, 页码 2817-2822出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/S0013-4686(02)00168-8
关键词
AlCl3-EtMeImCl room temperature molten salt; Al-La alloy; nucleation; surface morphology; orientation
The cathodic polarization curve on a tungsten disk electrode was measured in a LaCl3-saturated AICl(3)-EtMeImCl [1-ethyl-3-methylimidazolium chloride] melt (N = 0.667: N is molar fraction of AlCl3) at 298 K. The deposition overpotential of aluminum increases compared with the curve obtained before adding LaCl3. It was found that the nucleation/growth process is instantaneous nucleation from chronoamperometric data. When galvanostatic electrolysis was performed in the LaCl3-saturated melt, the strong ;orientation of (200) for the electrodeposits is observed at low current densities (less than or equal to 7.5 mA cm(-2)). On the other hand, the normalized integrated intensity of XRD for (200) and (220) reflections has similar strength at high current densities ( greater than or equal to 10.0 mA cm(-2)). The electodeposits become denser than those obtained in the original melt. In particular, very smooth surface is obtained in the case of 15.0 mA cm(-2) with stirring the bath. (C) 2002 Elsevier Science Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据