FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
卷 25, 期 8-9, 页码 765-773出版社
WILEY
DOI: 10.1046/j.1460-2695.2002.00574.x
关键词
axial loading; bearing steel; crack propagation; duplex S-N curves; fractography; long-life fatigue
Owing to difficult economical conditions, machines and structures often have to be used beyond the design lifetime. In this study, fatigue properties of a bearing steel in the long-life region were experimentally examined under cyclic axial loading. The complicated S-N behaviour was well explained as a combination of S-N curves for surface-induced fracture and interior inclusion-induced fracture. Fish-eye marks were always observed on the fracture surfaces of specimens, which failed in the latter fracture mode, and an inclusion was found at the center of the fish-eye. Finally, it was found that the fatigue fracture of this steel in the long-life region occurred through the following three processes: (i) formation of the characteristic area as a fine granular area (FGA), (ii) crack propagation to form the fish-eye and (iii) rapid crack propagation to cause the catastrophic fracture.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据