Low-temperature sintering and microwave dielectric properties of anorthite-based glass-ceramics

期刊

JOURNAL OF THE AMERICAN CERAMIC SOCIETY
卷 85, 期 9, 页码 2230-2235

出版社

AMER CERAMIC SOC
DOI: 10.1111/j.1151-2916.2002.tb00440.x

关键词

-

向作者/读者索取更多资源

TiO2 nucleated anorthite-based glass-ceramics were fabricated from glass powders. After sintering and crystallization heat treatment, various physical properties, including apparent bulk density and water absorption, were examined to evaluate the sintering behavior of anorthite-based glass-ceramic. Results showed that the complete-densification temperature for specimens was as low as 900degreesC. Sufficient crystallization was achieved by subsequently raising the firing temperature to 950degreesC, and the dielectric quality factor was promoted to the maximum value. Contents of nucleating agent (TiO2) played an important role in the dielectric constants. The crystallinity was controlled by raising the firing temperature at a constant heating rate. The degree of crystallization affected the dielectric properties of sintered glass-ceramics. At the resonant frequency of 10 GHz, anorthite glass-ceramics with 5 wt% TiO2 possessed the lowest permittivity of 8 and exhibited appropriate dielectric properties as compared with those with B2O3 and 10 wt% TiO2.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.7
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据