We report the surface, structural, and optical properties of typical Ga- and N-polar GaN films grown on sapphire substrates by molecular beam epitaxy. The Ga-polar films were grown on AlN buffer while the N-polar films were grown on GaN buffer layers. Atomic force microscopy imaging shows that the as-grown and chemically etched Ga-polar films have a flat and pitted surface while the N-polar surface is rougher with isolated columns or islands. Transmission, electron microscopy demonstrates a low density of inversion domains in the Ga-polar films, while a much higher density of inversion domains was observed in the N-polar films. X-ray diffraction curves show a narrower (002) peak for Ga-polar films than that for N-polar films. On the other hand, both Ga- and N-polar films show a similar width of (104) peak. Despite their rough surfaces, high density of inversion domains, and broader (002) x-ray diffraction peaks, N-polar films with low dislocation density were demonstrated. In addition, higher PL efficiency for the N-polar films than that for the Ga-polar films was observed. (C) 2002 American Vacuum Society.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据