SOLID STATE IONICS
卷 151, 期 1-4, 页码 413-418出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/S0167-2738(02)00547-7
关键词
powder synthesis; niobate; LiNbO3; butanedioc acid; hydroxy; malic acid
Pure lithium niobate (LN) powders were prepared by a wet-chemical method. Hydrated niobium oxide was dissolved in a hot aqueous solution of oxalic acid, followed by the precipitation of mobic acid by the addition of ammonia solution until pH =11. Niobic acid precipitated was dissolved in an aqueous solution of DL-malic acid. A small amount of the Nb-malic complex synthesized was isolated and characterized by thermogravimetry (TG) and infrared (IR) spectroscopy, and the molecular composition of the complex was determined as H[Nb2O(H3C4O5)(3)]. The exact content of niobium in the stable solution of Nb-malic solution was determined by gravimetric analysis. Stoichiometric amount of lithium carbonate was added into Nb-malic solution. After the solvent elimination, the remaining solid powder was calcined at 350 degreesC, ground and calcined over a temperature range from 300 to 900 degreesC. Calcined powders were characterized by X-ray diffraction (XRD) and Raman spectroscopy. Crystalline LN phase was identified at 500 degreesC/2 h, although the total elimination of the inorganic carbon occurred only at 650 degreesC/2 h. (C) 2002 Published by Elsevier Science B.V.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据