JOURNAL OF ENDODONTICS
卷 28, 期 12, 页码 828-830出版社
LIPPINCOTT WILLIAMS & WILKINS
DOI: 10.1097/00004770-200212000-00008
关键词
-
The purpose of this study was to determine if calcium hydroxide, mineral trioxide aggregate, or sodium hypochlorite caused a change in the force required to fracture root dentin. Ten bovine central and lateral incisors were machined using various saws and drills to produce a cylinder of dentin with a 6.0-mm outer diameter 3.5-mm inner diameter and a length of 10 mm. The cylinders were cut lengthwise into four symmetrical pieces. The canal sides of the sections were then placed into Petri dishes containing a 1-mm depth of calcium hydroxide, mineral trioxide aggregate, sodium hypochlorite, or physiologic saline (control). The samples remained in the dishes for 5 weeks and were then shear tested by using an Instron machine. Data were analyzed using an ANOVA test for comparison of the groups as a whole, and a t test was used to compare each quarter section with its control from the same tooth. A 32% mean decrease in strength was discovered for calcium hydroxide, a 33% decrease in strength for mineral trioxide aggregate, and a 59% decrease for sodium hypochlorite. All decreases in strength were statistically significant: p < 0.001 for calcium hydroxide, p = 0.027 for mineral trioxide aggregate, and p < 0.001 for sodium hypochlorite. Results indicated that root dentin was weakened after 5 weeks of exposure to calcium hydroxide, mineral trioxide aggregate, or sodium hypochlorite.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据