Microstructures developed in commercial 15-5 PH precipitation-hardened stainless steel after different heat treatments have been studied. In the as received condition, two types of carbides, NbC and M7C3, were present. Age hardening involves initial formation of fine precipitates rich in copper. Conventional transmission electron microscopy (TEM) and high resolution electron microscopy (HREM) studies have revealed the formation of a 9R structure copper precipitates (4 nm) in the samples aged at temperatures below 500 degreesC. However, at higher temperatures, in addition to the formation of these precipitates, the austenite phase was formed. After ageing at 500 degreesC for 128 h, M23C6 carbides were observed. The majority of the M23C6 carbides were in the interface of martensitic matrix and retained austenite. A second type of copper precipitate being, spherical in shape, were observed on ageing at 650 degreesC. TEM and X-ray microanalysis on thin foils and on carbon extraction replicas used for analysing the structure and metallic compounds of these precipitates. The mechanical properties following strain deformation has been carried out using scanning electron microscope (SEM), TEM and HREM. At peak aged, the 15-5 PH alloy exhibit brittle failure, the major fracture mode was cleavage and/or quasicleavage. (C) 2002 Elsevier Science B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据