JOURNAL OF BIOMEDICAL MATERIALS RESEARCH
卷 62, 期 4, 页码 558-566出版社
JOHN WILEY & SONS INC
DOI: 10.1002/jbm.10284
关键词
poly(propylene fumarate-co-ethylene glycol); hydrogel; hydrophilicity; cell adhesion
资金
- NIDCR NIH HHS [R01 DE 13031] Funding Source: Medline
We synthesized poly(propylene fumarate-co-ethylene glycol) block copolymers [P(PF-co-EG)] that were crosslinked to form hydrogels and investigated the effect of copolymer composition on cell adhesion to the hydrogels. These copolymers were water soluble when the molar ratio of ethylene glycol repeating unit to propylene fumarate repeating unit was higher than 4.4. The water content of swollen hydrogels increased from 29 to 63% and the water contact angle decreased from 38 to 21degrees as the molar ratio increased from 0.6 to 4.4. No significant change in either property was observed for ratios higher than 4.4. In a cell adhesion assay under serum-free conditions, the number of adherent platelets and smooth muscle cells decreased from 21 to 2% and from 78 to 20% of the initial seeding density, respectively, as the molar ratio increased from 0.6 to 7.8. Adherent smooth muscle cells did not spread on the hydrogels of the compositions tested. Adherent platelets did not show any filopodia. These results suggest that the hydrophilicity of P(PF-co-EG) hydrogels is one of the factors affecting cell adhesion, and that copolymer modification may be required for enhancing cell adhesion for an application involving the copolymers as in situ crosslinkable cell carriers. (C) 2002 Wiley Periodicals, Inc.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据