期刊
SURFACE & COATINGS TECHNOLOGY
卷 165, 期 3, 页码 232-240出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/S0257-8972(02)00733-8
关键词
anodic oxide layers; aluminum; current waveforms; microhardness; surface roughness
Anodic oxidation of Al, AlSi10 and AlSi10Cu3 permanent mold cast substrates in 2.25 M H2SO4, at 0 degreesC for 50 min using different current waveforms (i.e. square, ramp-square, ramp-down and ramp-down spike) was performed, in an attempt to evaluate the effects of pulsed current on layer growth and properties. The pulses were unipolar and superimposed (amplitude ratio 4:1), applied with a frequency of 0.0125 Hz and a duty cycle of 75%. The same average current densities (i.e. 3.0 and 4.2 A dm(-2)) were imposed for all waveforms. The results on voltage transients, layer thickness, morphology, microhardness (HV0.025) and surface roughness (R-a) have been compared to the results obtained when direct and ramped current were applied. Voltage transients followed the current waveforms to a certain extent depending on the waveform shape and substrate composition. The differences obtained in layer properties were not statistically different relative to the direct current experiments and remained dependent mainly on substrate composition. (C) 2002 Elsevier Science B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据