BIOMATERIALS
卷 24, 期 6, 页码 1047-1057出版社
ELSEVIER SCI LTD
DOI: 10.1016/S0142-9612(02)00434-9
关键词
chitosan; polyglycolide; porous matrix; tissue engineering
Polyglycolide (PGA) and chitosan mixture solution was prepared using solvents of low toxicity to create novel, porous, biocompatible, degradable, and modifiable hybrid matrices for biomedical applications. The porosity of these PGA-chitosan hybrid matrices (P/C matrices) was created by a thermally induced phase separation method. Two types of the P/C hybrid matrices containing 70wt% PGA (P/C-1 matrix) and 30wt% PGA (P/C-2 matrix) were fabricated. Chitosan matrix was also prepared for comparison. A 35-day in vitro degradation revealed that the weight losses for the P/C-1 and P/C-2 matrices were similar (similar to 61%), but the releases of glycolic acid from the P/C-1 and P/C-2 matrices were 95% and 60%, respectively. The P/C-1 matrix had higher porosity and higher mechanical strength than the P/C-2 and chitosan matrices. Fibroblast cells cultivated in these matrices proliferated well and the cell density was the highest in the P/C-1 matrix, followed by the chitosan and P/C-2 matrices, suggesting good biocompatibility for the P/C-1 matrix. We thereby concluded that the P/C-1 matrix, due to its high strength, porosity, biocompatibility and degradability, is a promising biomaterial. The presence of chitosan in the P/C matrices provides many amino groups for further modifications such as biomolecule conjugation and thus enhances the application potential of the P/C hybrid matrices in tissue engineering. (C) 2002 Elsevier Science Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据