CHEMISTRY OF MATERIALS
卷 15, 期 8, 页码 1676-1681出版社
AMER CHEMICAL SOC
DOI: 10.1021/cm021027f
关键词
-
Films and 200-nm wire arrays of Bi1-xSbx alloys, one of the best known low-temperature thermoelectric materials, have been obtained by electrodeposition without the need for complexing the Sb cations in solution or further thermal treatment after deposition. The process consists of reduction of Bi1-xSbx directly from a solution of Bi(NO3)(3) . 5H(2)O and SbCl3 in dimethyl sulfoxide at 25 degreesC on Pt electrodes. The electrodeposited films are polycrystalline and single phase under slow growth conditions, but two phases are observed under rapid growth conditions (more negative potentials) and for films with roughly equal amounts of Bi and Sb. 200-nm wire arrays of Bi1-xSbx were grown under similar conditions using porous alumina as a template. Arrays of dense, continuous, and highly crystalline Bi0.84Sb0.16 wires (close to the predicted optimum composition for thermoelectric applications) have been fabricated successfully at deposition potentials of -0.28 V vs Ag/AgCl from a solution of 0.050 M Bi and 0.030 M Sb in DMSO.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据