JOURNAL OF ALLOYS AND COMPOUNDS
卷 620, 期 -, 页码 185-191出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2014.09.056
关键词
Thin films; Vapor deposition; AFM; Electrical properties and photoelectron spectroscopies; Solar cells
资金
- SASTRA University
The influence of substrate temperature on the microstructural behavior, optical, electrical properties and on the scattering mechanism of charge carriers were studied for the as-prepared radio-frequency (R-F) magnetron sputtered Cadmium Tin Oxide (Cd2SnO4) thin films. Films prepared at the substrate temperature of 300 degrees C were found to be polycrystalline in nature with preferential orientation along (311) plane. Well pronounced Moss-Burstein shift, in the transmittance spectra with dispersions in the optical band gap from 3.07 to 3.30 eV, was observed at substrate temperatures between 25 and 300 degrees C. Optical property of high visible transmittance was retained by the films. Analysis of the electrical properties on the prepared crystalline Cd2SnO4 films showed a calculated resistivity of 10 (3)-10 (4) Omega cm, with n-type carrier density in the range of 10(19)-10(20) cm (3) and the charge carrier mobility in the range of 6330 cm(2)/V s. The effects of structural, compositional and optical properties on the scattering mechanism of charge carrier are elaborated and reported to be an experimental evidence for the theoretical predictions. The results revealed the essential DC electrical conduction behavior, which is ideal for the fabrication of Cd2SnO4 based CdS/CdTe thin film solar cells. (C) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据