supercapacitor; ammoxidation; active carbon; pseudocapacitance
Modification of active carbon by ammoxidation was used to obtain electrode material with intermediate acidic-basic properties. It allowed advantage to be taken of the pseudocapacitance characteristics of the material for the improvement of the supercapacitor. Precursor fabric from regenerated cellulose was subjected to carbonization, followed by steam activation at 400 and 800 degreesC, respectively. Ammoxidation was carried out with a mixture of ammonia and air at a ratio of 1:3 in a flow reactor at 250 degreesC at different stages of the process, i.e. before or after carbonization, or after activation. Active materials were described with respect to microporous structure (nitrogen adsorption), chemical composition (elemental analysis and XPS) and investigated by electrochemical methods (cyclic voltammetry, galvanostatic charge/discharge and impedance spectroscopy) in acidic (4 M H2SO4) and alkaline (7 M KOH) media. The electrochemical behavior of individual samples is discussed from the viewpoint of the diverse electron-donor properties of the functional groups of both nitrogen and oxygen heteroatoms which result from different technological processing conditions. (C) 2003 Elsevier Science Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据