Copper tin sulfide thin films have been grown on soda-lime glass substrates from the elemental constituents by co-evaporation. The synthesis was performed at substrate temperatures of 350 degrees C and 450 degrees C and different Cu/Sn ratios, adjusting the deposition time in order to obtain thicknesses above 1000 nm. The evolution of the morphological, structural, chemical, optical and electrical properties has been analyzed as a function of the substrate temperature and the Cu/Sn ratio. For the samples with Cu/Sn <= 1, Cu2Sn3S7 and Cu2SnS3 have been observed by XRD. Increasing the Cu/Sn to 1.5, the Cu2SnS3 phase was the majority, being the formation completed at Cu/Sn ratio around 2. The increment of the substrate temperature leads to a change of cubic structure to tetragonal of the Cu2SnS3 phase. The chemical treatment with KCN was effective to eliminate CuS excess detected in the samples with Cu/Sn > 2.2. The samples with Cu2SnS3 structure show a band gap energy increasing from 0.9 to 1.25 eV and an electrical resistivity decreasing from 7 * 10 (2) Omega cm to 3 * 10 (3) Omega cm when the Cu/Sn atomic ratio increases from 1.5 to 2.2. (C) 2015 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据