JOURNAL OF POWER SOURCES
卷 119, 期 -, 页码 84-87出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/S0378-7753(03)00130-7
关键词
intermetallic; anode; lithium battery; aluminium alloy
The electrochemical performance of Fe2Al5 was investigated as an anode material for lithium-ion batteries. Fe2Al5 was prepared by arc melting the constituent elements, crushing to a suitable size and then ball milling. By removing samples from the ball mill at various times the effect of milling time on the electrochemical properties was examined. The highest discharge capacity (485 mAh/g) observed was as a result of ball milling for 10,000 min which is consistent with the theoretical capacity for formation of AlLi (543 mAh/g). Cyclic voltammetry and differential capacity plots, however, do not offer conclusive evidence of the formation of AlLi. Both charge and discharge capacity improved with increasing milling but cycle life remained poor. Removal of lithium from the structure was difficult with charge capacities being quite low. The first charge capacities for instance were in the range of 20-40% of the first discharge capacity. (C) 2003 Elsevier Science B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据