Synthesis and characterization of chondroitin sulfate-methacrylate hydrogels

The various degree of methacrylate (MA) substitution on chondroitin sulfate. (CS) was prepared by reacting chondroitin sulfate with methacrylic anhydride (MAA) in the presence of sodium hydroxide (NaOH) as a base. The effects of reaction time, reaction temperature, MAA concentration, and NaOH amount on the substitution degree of CS-MA were tested. The confirmation of the CS-MA chemical structure was carried out by H-1-NMR, C-13-NMR, FTIR and the degree of MA substituent on CS was calculated from the ratios of two peak intensities corresponding to methyl groups on methacrylate and chondroitin sulfate, respectively. Hydrogels were prepared by free radical polymerization of CS-MA precursors with or without acrylic acid (AA). CS-MA hydrogels were easily broken into small pieces during swelling study. However, CS-MA-AA hydrogels remained completely and showed a range of swelling ratio from 200 to 390% and exhibited an increase in swelling ratio with a decreasing degree of MA substitution. The thermal degradability observed with a TGA explained the unstableness of these hydrogels in comparison with the puree CS. The surface morphology conducted by SEM exhibited a porous structure after swelling. (C) 2003 Elsevier Science Ltd. All rights reserved.