Hot pressing; Optical properties; Mechanical properties; Phosphor; Sialon
资金
- Global Research Laboratory (GRL) program of the National Research Foundation of Korea (NRF) - Ministry of Education, Science and Technology (MEST), Republic of Korea [2010-00339]
Thin transparent yellow phosphor Sialon ceramics were fabricated by hot pressed sintering method. The fabricated Sialon ceramics were co-doped with Eu2O3 and its yellow luminescence was observed around 570 nm wavelength when excited by UV to blue light spectrum. Furthermore, the white light was observed when thin yellow phosphor Sialon plates were coupled with blue led (455 nm). From XRD patterns, major alpha-Sialon phase and a minor beta-Sialon phase were observed with the addition of Eu2O3. The microstructure revealed that the average grain size was below 500 nm and other phases like AIN polytypoids exists as minor phase. Small amount of Y2O3 addition significantly increased the luminescence intensity as compared to only Eu2O3 addition. Sialon ceramics are generally known as advanced ceramics for high temperature applications; the fabricated transparent yellow Sialon phosphor also exhibits good mechanical properties and suitable for remote phosphor. (C) 2015 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据