JOURNAL OF ALLOYS AND COMPOUNDS
卷 627, 期 -, 页码 324-332出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2014.11.213
关键词
Magnesium alloys; Aging; Precipitation; Extrusion; Dynamic recrystallization
资金
- Korean Ministry of Knowledge Economy [10037928]
The effect of aging prior to extrusion (APE) on the microstructure and mechanical properties of Mg-7 Sn-1Al-1Zn (wt.%) alloy was investigated under various extrusion conditions. The extruded alloy exhibited a partially or fully recrystallized (DRXed) structure with fine Mg2Sn precipitates, with the fraction and size of the DRXed grains decreasing with a reduction in extrusion temperature and ram speed. The numerous precipitates formed by APE also reduces the size of the DRXed grains and increases the overall amount of precipitate in the extruded alloy, thereby improving the yield and tensile strength regardless of the extrusion conditions. The ductility of the alloy was also improved by APE when extruded at relatively high temperature and speed, which is attributed to the suppressed formation of coarse banded Mg2Sn; however, a deterioration in ductility was observed at low ram speed and/or low extrusion temperature due to the reduction in the fraction of DRXed grains and increased amount of Mg2Sn precipitates. Furthermore, the extruded alloy with APE showed superior strength and ductility to that aged after extrusion, indicating that APE is the more effective means of improving the mechanical properties of extruded alloy. (C) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据