Bismuth layer-structured; Piezoelectric ceramics; Microstructure; Na0.25K0.25Bi2.5Nb2O9
资金
- National Natural Science Foundation of China [NSFC11304327, 51201175, 11234012, 11204326]
- Ningbo Municipal Natural Science Foundation [2014A610003, 2014A610007, 2014A610008, 2014A610011, 2014A610014, 2014A610122]
The effects of cobalt addition on the properties of Na0.25K0.25Bi2.5Nb2O9 (NKBN) ebased ceramics have been investigated in details. It was found that the ceramics possess a pure phase of bismuth oxide layer etype structure. The Curie temperature T-c gradually increases from 653 degrees C to 662 degrees C with increasing the Co modification. The electrical properties of NKBNebased ceramics are improved significantly by the addition of Co. The piezoelectric constant d33, dielectric loss tan d, mechanical quality factor Q(m) and remanent polarization Pr for the NKBN ceramics with 0.20 wt% Co2O3 modification were found to be 23 pC/N, 0.35%, 3028, 12.03 mC/cm(2), respectively. Thermal annealing studies indicated that the cobalt emodified NKBN ceramics system possesses stable piezoelectric properties, demonstrating that the cobaltemodified NKBNebased ceramics are the promising candidates for highetemperature applications. (C) 2015 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据