期刊
JOURNAL OF BIOMECHANICS
卷 36, 期 7, 页码 973-980出版社
ELSEVIER SCI LTD
DOI: 10.1016/S0021-9290(03)00066-6
关键词
microcrack; propagation; accumulation; osteon; barrier
Fatigue damage in bone occurs in the form of microcracks. This microdamage contributes to the formation of stress fractures and acts as a stimulus for bone remodelling. A technique has been developed, which allows microcrack growth to be monitored during the course of a fatigue test by the application of a series of fluorescent chelating agents. Specimens were taken from bovine tibiae and fatigue tested in cyclic compression at a stress range of 80 MPa. The specimens were stained before testing with alizarin and up to three other chelating agents were applied during testing to label microcracks formed at different times. Microcracks initiated in interstitial bone in the early part of a specimen's life. Further accumulation of microcracks is then suppressed until the period late in the specimen's life. Microcracks were found to be longer in the longitudinal than in the transverse direction. Only a small proportion of cracks are actively propagating; these are longer than non-propagating cracks. These results support the concept of a microstructural barrier effect existing in bone, whereby cracks initiate easily but slow down or stop at barriers such as cement lines. (C) 2003 Elsevier Science Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据