Pb-free solder; electrical resistivity; heat treatment; microstructure
Solder joints were prepared from seven eutectic and near-eutectic Sn-based compositions and characterized for electrical resistivity after 100 h and 1,000 h of isothermal aging at 423 K. The solder joint samples were prepared by hand soldering to copper substrates, and the post-heat treatment resistivity was measured at room temperature in a specially designed, four-point probe fixture. Compositions tested included Sn-3.5Ag, Sn-3.7Ag-0.9Cu, Sn-3.7Ag0.5Cu, Sn-3.6Ag-1.0Cu, and Sn-3.9Ag-0.6Cu. In addition, the effect of a minor addition of a fourth element, designed to improve high-temperature shear strength, was also evaluated in the compositions Sn-3.7Ag-0.6Cu-0.3Co and Sn-3.7Ag-0.7Cu-0.2Fe. The observed changes in electrical resistivity are discussed in terms of microstructural coarsening, diffusional transport from the substrate, and nucleation of precipitate phases.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据