pseudocapacitive behavior; NiO; RuO2; electrochemical capacitor; composite
NiO/RuO2 composite materials were prepared for use in electrochemical capacitors (ECs) by co-precipitation method followed by heat treatment. X-ray diffraction (XRD) spectra indicated that no new structural materials were formed and ruthenium oxide particles were coated by NiO particles. RuO2 partly introduced into NiO-based electrode had improved its electrochemical performance and capacitive properties by using electrochemical measurements. A maximum specific capacitance of 210 F/g was obtained for NiO-based composite electrode with 10 wt.% RuO2 in the voltage range from -0.4 to 0.5 V in 1 mol/1 KOH solution. By comparison of effect of modified modes on the specific capacitance, chemically modified composite electrodes had more stable cycling properties than those of physically modified electrodes. After 200 cycles, specific capacitance of NiO-based chemical composite electrode with 5 wt.% RuO2 kept 95% above, while that of physical electrode was only 79% of initial specific capacitance. (C) 2003 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据