期刊
JOURNAL OF PHOTOCHEMISTRY AND PHOTOBIOLOGY A-CHEMISTRY
卷 161, 期 2-3, 页码 105-110出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/S1010-6030(03)00280-6
关键词
dye-sensitized; tin oxide; surface modification; nanocrystalline; thickness effect
Zinc-modified nanocrystalline SnO2 electrodes are prepared by chemical treatment of the commercial SnO2 colloid with zinc acetate and their thickness effects on photovoltaic characteristics are investigated. Open-circuit voltage (V-oc) and fill factor increase with increasing zinc concentration, while short-circuit photocurrent (J(sc)) decreases. The normalized incident photon-to-current conversion efficiency (IPCE) shows that increase of zinc concentration utilizes long wavelength light. Concerning the conversion efficiency, optimal concentration within the present experiment is found to be 10 mol.% Zn2+ with respect to Sn4+. As increasing thickness of the films based on 10 mol.% zinc-modified SnO2 ranging from 0.76 to 8.12 mum, J(sc) increases, reaches maximum and then decreases without change in (Vo)c. The highest conversion efficiency of about 3.4% is achieved under 1 sun of AM 1.5 irradiation for the similar to6.3 mum-thick 10 mol.% zinc-modified SnO2 film with J(sc) of 9.09 mA/cm(2). V-oc 600 mV and fill factor 62%. (C) 2004 Elsevier B.V. All fights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据