poly(propylene) (PP); nanocomposites; crystallization; DSC; graft copolymers
Nano-CaCO3 /polypropylene (PP) composites modified with polypropylene grafted with acrylic acid (PP-g-AA) or acrylic acid with and without dicumyl peroxide (DCP) were prepared by a twin-screw extruder. The crystallization and melting behavior of PP in the composites were investigated by DSC. The experimental results showed that the crystallization temperature of PP in the composites increased with increasing nano-CaCO3 content. Addition of PP-g-AA further increased the crystallization temperatures of PP in the composites. It is suggested that PP-g-AA could improve the nucleation effect of nano-CaCO3. However, the improvement in the nucleation effect of nano-CaCO3 would be saturated when the PP-g-AA content of 5 phf (parts per hundred based on weight of filler) was used. The increase in the crystallization temperature of PP was observed by adding AA into the composites and the crystallization temperature of the composites increased with increasing AA content. It is suggested that the AA reacted with nano-CaCO3 and the formation of Ca(AA)(2) promoted the nucleation of PP. In the presence of DCP, the increment of the AA content had no significant influence on the crystallization temperature of PP in the composites. (C) 2003 Wiley Periodicals, Inc.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据