barium titanate; domain engineering; domain size; piezoelectricity; single crystals
Engineered domain configurations with different domain sizes were induced in [111]c oriented tetragonal barium titanate BaTiO3 single crystals, and their piezoelectric properties investigated as a function of domain size. Prior to this study, the dependence qf domain configuration on temperature and electric field E was investigated using polorised light microscopy to establish the optimum conditionsfor domain size control. As a result, above the Curie temperature T-c qf 132.2degreesC, when E greater than 6 kV cm(-1) was applied along the [111](c) direction, an engineered domain configuration with fine domain structure appeared. Moreover, it was alsofiound that this fine domain structure was still stable at room temperature in the absence oj'electric field. Finally, the piezoelectric properties were measured using 31 resonators with three domain sizes, and it was found that piezoelectric properties such as d(31) and k(31) increased significantly with decreasing domain size.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据