The effects of composition and preparation temperature on the structure of LiMgyNi0.5-yMn1.5O4 (y = 0, 0.25, 0.5) compounds are studied by EPR, FTIR, X-ray, and neutron diffraction. For y greater than or equal to 0.25, cation ordering in a P4(3)32 superstructure takes place on increasing the annealing temperature from 450 to 750 degreesC. In contrast, a loss of octahedral cation ordering and partial reduction of transition metals are found for LiNi0.5Mn1.5O4 when preparation temperature increases from 700 to 800 degreesC. The EPR behavior of LiMg0.5Mn1.5O4 is determined from localized Mn4+ ions, whereas residual antiferromagnetic correlations between Ni2+ and Mn4+ ions give rise to strong resonance absorption for LiNi0.5Mn1.5O4. The magnetic dilution of the Ni2+ sublattice by Mg2+ or Mg2+/Ni2+ causes strong changes in an apparent g-factor, whereas the line width undergoes little changes. When LiMgyNi0.5-yMn1.5O4 oxides are used as positive electrode materials in test lithium anode cells, the capacity in the 5-V region decreases with decreasing Ni content. Nevertheless, cycling in the 3-V region showed a net improvement on increasing Mg content. Lithium extraction from LiNi0.5Mn1.5O4 (up to 70%) leads to a loss of intensity in the EPR signal as a consequence of the oxidation of paramagnetic Ni2+ to diamagnetic Ni4+ without significant changes in local environment of Mn4+. For fully delithiated Li1-xNi0.5Mn1.5O4 oxide, the EPR spectrum from localized Mn4+ ions is observed, indicating an exhaustion of paramagnetic Ni2+ ions in the vicinity of Mn4+ ions.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据