New lead-free relaxors based on the K0.5Na0.5Nb0.30-SrTi0.3 solid solution

New lead-free relaxors have been produced from the K0.5Na0.5NbO3-SrTiO3 (KNN-STO) system. The solid solubility within the studied range of compositions (1 - x) K0.5Na0.5NbO3-xSrTiO(3) was observed for x up to 0.33. A pseudo-cubic perovskite structure was determined for x = 0.15 to 0.25. The high density and the uniform distribution of fine grains and pores were confirmed by the translucency of these ceramics. The 0.85KNN-0.15STO composition reaches the dielectric permittivity of above 3000 at room temperature. Dielectric spectroscopy measurements revealed that, as with lead-based complex perovskites, the cationic distribution disorder is reflected in relaxorlike properties, thus suggesting possible applications based on this environmentally friendly lead-free ceramic system.