期刊
ACTA CRYSTALLOGRAPHICA SECTION B-STRUCTURAL SCIENCE CRYSTAL ENGINEERING AND MATERIALS
卷 60, 期 -, 页码 282-286出版社
INT UNION CRYSTALLOGRAPHY
DOI: 10.1107/S0108768104007475
关键词
-
The crystalline structures of the superionic high-temperature copper selenides Cu2-xSe (0 < x < 0.25) produced using mechanical alloying were investigated using X-ray diffraction (XRD). The measured XRD patterns showed the presence of peaks corresponding to the crystalline superionic high-temperature alpha-Cu2Se phase in the as-milled sample, and its structural data were determined by means of a Rietveld refinement procedure. After heat treatment in argon at 473 K for 90 h, this phase transforms to the superionic high-temperature alpha-Cu1.8Se phase, whose structural data were also determined by Rietveld refinement. In this phase, a very low occupation of the trigonal 32(f) sites (similar to 3%) by Cu ions is found. In order to explain the evolution of the phases in the samples, two possible mechanisms are suggested: (i) the high mobility of Cu ions in superionic phases and (ii) the important diffusive processes in the interfacial component of samples produced by mechanical alloying.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据